Elaboration and corrosion resistance of self-assembled 2,5-bis(4-pyridyl)-1,3,4-oxadiazole film on carbon steel: Surface characterisations, electrochemical assessments and surface pre-treatment effect

Résumé

The self-assembled monolayers (SAMs) of 2,5-bis(4-pyridyl)− 1,3,4-oxadiazole (4-POX) were formed on carbon steel (CS) surface to improve the corrosion resistance of the substrate in 1 M HCl medium. The structural characterisations of 4-POX/SAMs films were performed by using Fourier transform infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS), Scanning Electron Microscopy (SEM), and contact angle measurements. The protection ability of SAM films against CS-substrate corrosion in 1 M HCl was studied using potentiodynamic polarization and AC impedance techniques. FTIR and XPS results showed that the 4-POX molecules adsorbed on the CS surface, and the contact angle values on the modified surface supported the formation of hydrophobic 4-POX/SAMs. The results of electrochemical measurements indicated, when the self-assembling time increased, the corrosion resistance od 4-POX/SAMs film enhaced, reaching a maximum protection efficiency value of 94.6% for 6 h of self-assembly. Different kinds of surface pre-treatments (amorphous phosphatation (Pa), APTES (PAPTES), and N2 plasma (PN2)) of CS-substrate were then applied in order to improve the corrosion resistance of SAM process.

Domaines

Fichier principal
Vignette du fichier
S2352492823010735.pdf (2.8 Mo) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)
Licence

Dates et versions

hal-04130920 , version 1 (09-07-2025)

Licence

Identifiants

Citer

Imane Nadi, Marya Bouanis, Khadija Nohair, Abdelhamid Nyassi, Abdelkader Zarrouk, et al.. Elaboration and corrosion resistance of self-assembled 2,5-bis(4-pyridyl)-1,3,4-oxadiazole film on carbon steel: Surface characterisations, electrochemical assessments and surface pre-treatment effect. Materials Today Communications, 2023, Materials Today Communications, 35, pp.106382. ⟨10.1016/j.mtcomm.2023.106382⟩. ⟨hal-04130920⟩
84 Consultations
64 Téléchargements

Altmetric

Partager

  • More